J4 ›› 2010, Vol. 27 ›› Issue (3): 257-263.

• Spectrascopy •     Next Articles

Afterglow and Thermoluminescence spetrum Of SrAl2O4:Eu2+ and SrAl2O4:Eu2+,Dy3+*

DENG Liu-yong, HU Yi-hua, WANG Yin-hai,WU Hao-yi,XIE Wei   

  1. School of Physics and Optoelectronic Engineering, Guangdong University of Technology, Guangzhou 510006, China
  • Received:2009-06-16 Revised:2009-09-08 Published:2010-05-28 Online:2010-05-11

Abstract:

The properties of afterglow and thermoluminescence spetrum between SrAl2O4:Eu2+and SrAl2O4:Eu2+,Dy3+ are presented and the influence on traps level of SrAl2O4:Eu2+ by codoping Dy3+ is also studied in this paper. From the XRD and Photoluminescence result, the crystal phase and light centre together with emission spetrum can not be changed by codoping Dy3+. From the result of comparison of thermoluminescence properties of SrAl2O4:Eu2+ and SrAl2O4:Eu2+,Dy3+ with different delay time, it is known that the density of the original shallow traps is increased by the codopant of Dy3+,that can enhance the persistent luminescence properties. And also the electrons transfer from the shallow trap to deeper one can be seen from the peak fitting result of thermoluminescence spectrum with diverse delay time. The different decay property with different trap levels at room temperature is the reason for the complicated a long afterglow rule.

Key words: materials∣trap levels∣SrAl2O4∣long afterglow∣thermoluminescence